The Effect of the Residual Stress Which is Induced by Shot Peening at Water Cooling Hole on the Die-casting Die

marzo 17, 2021

Y. Kobayashi, Manager, Development group, Sintokogio, LTD., Nagoya Japan

Abstract

The temperature of the die-casting die should be kept lower than molten aluminum during processing die-casting. This method is used in order to prevent adhesion between die material and aluminum molten. Therefore, water-cooling holes dissipate heat to cool the die. Usually, water-cooling holes carry out from the backside of the die.

Tensile stress will occur at the surface of water-cooling hole, not only the top area but also the side area due to the temperature drift between die and water.  As a result, water-cooling hole will crack due to stress corrosion cracking and fatigue by cyclic thermal stress cycling. Usually, the minimum diameter of water-cooling hole is 3mm and the maximum hole depth is 300mm.

Shot peening is one of the methods used to improve fatigue strength inducing plastic deformation. In this study, shot peening effect is carried out to prevent stress corrosion cracking on water cooling hole and tested to analyze any benefit.

In the previous experiment, 1500MPa residual stress was induced on the inside of the water-cooling hole. Finally, extension of die life that was achieved by applying shot peening can be confirmed in actual production.

Introduction 

The die-casting method enables the mass production of high-strength, high-precision products at low cost. For this reason, it is used in many industries especially aluminum alloys for automotive parts due to high strength and lower weight of these alloys. 1)

In recent years, the thermal capacity of die casting dies increased due to the increasing size of die casting parts being cast.  As a result, quick cooling is required for product quality.  Quick cooling can help reduce costs by shortening cycle time.

The main failure point is toll cracks that is caused by heat checking on die casting die. These cracks will initiate at the boundary of crystal grain due to thermal stress and repetition by molten aluminum alloy. The recent problem is destructive to the water-cooling hole to cool the die-casting die. Generally, dies have holes drilled into them and the holes are filled with water after casting to help accelerate cooling.  The distance from the cavity’s surface to the water-cooling hole surface has become closer in order to decrease cooling time.  Due to this condition, tensile stress occurs at the surface of water-cooling holes due to cyclic heat stress.  Die cast users have reported issues of Stress Corrosion Cracking (SCC). 2)

Drilling water cooling holes and passages is very difficult because the diameter is very small, and the depth is very deep. Therefore, the inside wall is covered with a tool marks.

The tool mark forms a notch and it becomes the stress riser point. Therefore, it can be supposed that these become the factor in production of cracking.3)4)5)

Shot peening is one of the surface enhancement methods available to improve fatigue strength of metal parts due to inducing compressed residual stress. Stress corrosion cracking can be prevented with reduction of tensile stress. Therefore, this test was devised to determine if it is possible to prevent stress corrosion cracking by introducing residual stress utilizing the shot peening process.

In this research, we investigate how to use shot peening to increase residual stress in order to prevent stress corrosion cracking in the water-cooling hole of die casting dies.

Design of Experiments

In this research, the experiments are divided into two parts. Most die casting dies are nitriding after heat hardening and annealing. So, it is very hard material. The shot peening process inside the diameter of a long, thin hole in such a hard material is very difficult. At first, maximum residual stress is investigated on the material of die casting die as a pre experiment.

After that, shot peening is carried out to confirm the residual stress on a small diameter hole in order to investigate its residual stress. After selecting the optimum processing conditions by the experiment, shot peening is applied to the die casting die used in the actual operation to evaluate whether the water-cooling holes are strengthened.

TABLE 1 Chemical Composition (wt%)

CSiMnCrMoV
SKD610.41.00.45.21.20.8

Experiment#1   (PRE EXPERIMENT)

The target residual stress value on the inside of the water-cooling hole will be determined by pre experiment.

SKD61 hot working steel is chose for the specimen. It is typical steel for die casting dies. Table1 shows the chemical composition of the specimen. Specimens were heat hardened and nitrided.

Direct pressure shot peening equipment was used for experiment. 0.1MPa~0.4MPa air pressure were selected. Coverage is over 100%. Table2 show the hardness of shot media that was used in this experiment.

The shot peening carried out to the entire surface of the hole, which had a diameter of 5mm. The length of passage is 40mm.

TABLE 2 Hardness of Shot Media

Shot MediaABCD
Vickers Hardness70085012001350

After shot peening, residual stress, micro vickers hardness of the inside wall of cooling hole were measured. The compressive residual stresses was measured with the sin2θ-ψ method using X-rays. Table3 shows condition of X-ray measurement apparatus.

TABLE 3 Condition of X-ray Measurement Apparatus

Tube of X-rayCr-Kα
Diffraction planeαFe(211)
Tube voltage[kV]40
Tube current[mA]30
X-ray stress detectorPSPC
Diffraction angle of 2θ[deg]156.4
X-ray stress constant for sin2ψmethod[MPa/deg]-318
Irradiated area[mm]φ0.5

Maximum residual stress on the SKD61 (pre experiments)

Fig.1 shows residual stress that is obtained by each media. Because of the pre experiment, maximum residual stress is approximately 1600Mpa on this material. Therefore, target residual stress is 1500MPa for the inside of water-cooling hole.

DSCC Figure 1

Experiment #2  (Shot peening to water cooling hole)

Shot peening should be applied to the top and entire inside diameter surface of hole. Therefore, a rotating nozzle with a ricochet plate was developed. 6)

Fig.2 shows dimension of the specimen. Specimens are made of SKD61 which is the same material used for the pre-experiment. Nitriding was applied and was the same as the specimen of the pre experiment. After shot peening, the specimen was cut by a  micro cutter in order to measure the residual stress.

The same shot peening conditions were used as in the pre experiment. Fig.3 shows surface residual stress after shot peening by 1200HV media. «1T» indicates an arbitrary processing time, and 2T indicates twice the processing time. Similarly, 3T indicates three times the processing time. From Fig.3, there is proportional relationship between the processing time and surface residual stress.

Fig.4 shows surface residual stress after processing shot peening by 1350HV media. From Fig.4, there is negative proportional relationship between the processing time and surface residual stress.

The compressive residual stress value decreases as the processing time increases. After investigating, the surface is eroding. Also, surface residual stress was reduced with a longer processing time.

Fig.5 shows the surface residual stress of inside of the hole. The shot peening parameters were optimized for both the shot and media such as air pressure, flow rates, etc. Maximum residual stress is obtained when the highest hardness media was used.

Experiment #3 (Changing of tool mark)

Water cooling holes are thin and long, which makes it difficult to drill. In such cases, tool marks often remain on the surface after drilling. The tool mark may become the stress riser point that is caused by a cyclic heat change. Evolution of the tool marks are evaluated by photograph.

Specimens with a 5mm, 8.5mm, 11.5mm diameter hole were prepared for tool mark evaluation. The material is same as previous experiment.

Fig. 6 shows the change in appearance of the tool mark observed before and after shot peening. Before shot peening, the machined surface is covered with sharp edges. However, it can be seen that after shot peening, it has improved considerably. Therefore, it can be expected that the stress concentration is also alleviated.

Evaluation on Actual Production

So far, we have examined the effect of shot peening on water-cooling holes. The required effect of this method is to prevent damage to water cooling holes and extend the life of the die-casting die. This can only be evaluated in actual operation. Therefore, we carry out shot peening on the water-cooling holes of the mold that was actually used to verify whether the die life could be extended.

Fig.7 shows photograph of inside of the water-cooling hole that was used in actual production. Both dies used same number of cycles. The non-peened die was judged to require replacement. In addition, the shot peening performed was limited to areas where it is indicated in the photograph. In the case of the non-peened hole, a large crack developed. In the case of the shot peened hole, multiple small cracks developed on the surface where shot peening was applied. But the big crack appeared at non peened area. Therefore, some effect of shot peening is recognized.

Fig.8, Fig.9 shows cross sectional observations of the peened surface and the non-peened surface. In the case of the non-peened surface, a crack initiated to 8.5mm length. On the other hand, multiple small cracks and a long crack appeared. Long crack developed to a 4mm length. The lifetime can be estimated to be doubled as a result of shot peening. Therefore, the die lifetime expands as a result of residual stress that is induced by shot peening.

Conclusion 

・-1500MPa residual stress can be induced on the surface of water cooling hole that was heat hardened by shot peening.

・Increased die life as a result of shot peening can be confirmed in actual production.

References

  1. T. Hattori, “Strength Design Handbook for Failure Prevention of Products”, NTNTS(2012)
  2. K. Okubo, “Stress corrosion cracking and its measures”, Material. Vol.30 p.963 (1981)
  3. M. Hihara, “Life measures of the die-casting die”, Nikkan Kogyo Shimbun Ltd.(2003)
  4. Y. Tamura, “Die Steel for Die Casting with Higher Heat Cracking Resistance”, Hitachi Metals technical review, Vol.26 p.28 (2010)
  5. Japan society of shot peening, “Method and effect of shot peening”, Nikkan Kogyo Shimbun Ltd. (1997)
  6. K. Iwata, “Development of shot peening process by alley nozzle”, 53th plastic working(2002)